Eureka V2.0 Symmetry (12/26/2017) After the first prototype, I realized people will be tired out by the solid aluminum design's weight. I searched for a light and sturdy, yet stable and premium material. There were other candidates: cellulose, Acrylic, wood, PEEK, etc... however, the most reliable and durable, yet good looking one was for me, ebonite. Cellulose and acrylic looked fantastic. but cellulose was tricky material in t.. Eureka V1.0 Prototype Fountain Pen (2013) This is when the adventure of my fountain pen bagan! all the parts made of aluminum alloy. the nib was a conceptual design that i wanted to try. although it would write, since there was no tipping, it would wear out fast. i was hoping the oxidized aluminum would be thick and hard enough to prevent wear. in reality, it didn't work out so well. although it was a failure, it kick started my adventu.. (3G V1) Prototype Nib #9 (9/1/2019) Material: 14K Gold Basically same as #8, minus the material Mass production, not possible at the moment. hopely, I might be able to achieve some degree of production. in terms of writing function, the gold one is a bit stiffer than the argentium counterpart. also, more tarnish resistant. otherwise, similar in terms of function. Tested with V8.1 Asymmetrical (Urushi) Because this is a test, used .. Ebonite Feed 3rd. Gen V4.0, V5.0 Upgrade list 1) Differentiated comb thickness at front section (front side thicker then rear ones) 2) 5 turns of air/ink path (Most ebonite feeds 1 turn), stability increased. 3) micro slitting across the front part added, to inprove function and stability 4) tail thickness significantly increased to improve durability 5) feed overall thickness increased *below is the lastest version: 3G V5.0, n.. Ebonite Feed 3rd Gen. V2.0 (3/13/2019) modification to the previous version... 1) internal comb is thicker than external, therfore preventing brekage 0.6mm -> 1.2mm tested 10 times in and out. no breaking. 2) Slit thickness reduced in order to increase ink holding capacity. comb number increased to 30. 3) frontal combs added to further increase ink holding capacity. 4) front part sharper angle Analyzing Problem with 3rd Gen. Enonite feed (3/12/2019) 1) some fins break, when insertion and removal is repeated. this is a mojor problem, becuase some advanced users will inevitably remove the nib and feed. the underchannel + under fin structure design weakens certain portion of the feed significantly. even though the combs are 0.6mm thick to compensate for loss of structural integrity of the design, it simply isn't going to work. 2) the "tail" po.. Ebonite Feed 1st Gen. V1 (5-10-2018) This is my first ever created ebonite feed. The ebonite feed is naturally superior than plastic feeds, when it comes to wettability. The ebonite is made of natural rubber and sulfer + some additional stuff. The reason ebonite is wettable, is because of its high microscopic porosity. At the surface of the ebonite, the sulfer eventually dissipates into the air over time. when this sulfer is gone f.. Out of Stock Sorry, the product you selected is out of stock right now, we will try our best to make it available again. ... 이전 1 ··· 21 22 23 24 다음